Nature Transition Dental Zirconia Blank

Basic Information
Place of Origin: China
Brand Name: XTCERA
Certification: CE FDA
Model Number: 3D ML
Minimum Order Quantity: 50
Price: Negotiable
Packaging Details: Box
Delivery Time: 5-8 working days
Payment Terms: T/T
Supply Ability: 3000pcs/week
Detail Information
Strength: 1100MPa-750MPa Translucent: 43%-55%
Color: A3 Thickness: 16mm
Vickers Hardness: 1250HV Chemical Solubility: <100μg/m²
High Light:

full contour zirconia


pre sintered zirconia

Product Description

3D Multilayer Nature transition dental Zirconia Blanks with Tosoh zirconia powder


Simply to be Natural


Layer Proportion



Strength(MPa) Color Translucency
Layer 1 30% ≥1250 ≥750 ,≤1100





Layer 2 15%
Layer 3 15%
Layer 4 20%
Layer 5 20%



Natural Color Transition, Pre-colored.

Top High Transmittance with Natural Gradient

Simple and Less Process of Production


Available in all classic VITA 16 shades (A1 to D4)
XTCERA 3D multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three units, inlays, and onlays for anterior and posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.



Chemical Composition


ZrO2+HfO2 >94wt%
Y2O3 5.3wt%
AL2O3 <0.5wt%
Other Oxides <0.5wt%



Sintering Density :6.0g/cm³
Bending Strength:≥750MPa
Vickers Hardness:1250HV
Chemical Solubility:<100μg/m²



Sintering step Temperature range(℃) Time(h)
paragraph 1 20-900 1.5
paragraph 2 900-900 0.5
paragraph 3 900-1530 4.0
paragraph 4 1530-1530 2.0
paragraph 5 1530-800 2.0
paragraph 6 800-Natural cooling 100 Draw a charge