Nature Transition Dental Zirconia Blank

Basic Information
Place of Origin: China
Brand Name: XTCERA
Certification: CE FDA
Model Number: 3D ML
Minimum Order Quantity: 50
Price: Negotiable
Packaging Details: Box
Delivery Time: 5-8 working days
Payment Terms: T/T
Supply Ability: 3000pcs/week
Detail Information
Strength: 1100MPa-750MPa Translucent: 43%-55%
Color: A3 Thickness: 16mm
Vickers Hardness: 1250HV Chemical Solubility: <100μg/m²
High Light:

full contour zirconia

,

pre sintered zirconia


Product Description

3D Multilayer Nature transition dental Zirconia Blanks with Tosoh zirconia powder

 

Simply to be Natural

 

Layer Proportion

Vickers

Hardness(HV)

Strength(MPa) Color Translucency
Layer 1 30% ≥1250 ≥750 ,≤1100

Shallow

 

 

Deep

43%—55%
Layer 2 15%
Layer 3 15%
Layer 4 20%
Layer 5 20%

 

Characteristics:

Natural Color Transition, Pre-colored.

Top High Transmittance with Natural Gradient

Simple and Less Process of Production

 

Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA 3D multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three units, inlays, and onlays for anterior and posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.

 

 

Chemical Composition

 

ZrO2+HfO2 >94wt%
Y2O3 5.3wt%
AL2O3 <0.5wt%
Other Oxides <0.5wt%

 

Properties

Sintering Density :6.0g/cm³
Bending Strength:≥750MPa
Vickers Hardness:1250HV
Chemical Solubility:<100μg/m²

 

 

Sintering step Temperature range(℃) Time(h)
paragraph 1 20-900 1.5
paragraph 2 900-900 0.5
paragraph 3 900-1530 4.0
paragraph 4 1530-1530 2.0
paragraph 5 1530-800 2.0
paragraph 6 800-Natural cooling 100 Draw a charge