High Strength Dental Zirconia Blank For Milling Implant Crowns

Basic Information
Place of Origin: China
Brand Name: XTCERA
Certification: CE FDA ISO13485
Model Number: HT
Minimum Order Quantity: 10pcs
Price: Negotiable according to order quantity
Packaging Details: Box package
Delivery Time: 15 work days
Payment Terms: T/T, Western Union
Supply Ability: 1500Pcs /day
Detail Information
Density (after Sintering): 6.04g/cm³ Flextural Strength: 1250Mpa
Chemical Solubility: 64ug/cm² Vickers Hardness: 1298HV
CTE: 10±0.5 Radioactivity: 0.1Bq.q-1
High Light:

cad cam blanks

,

full contour zirconia


Product Description

Dental Zirconia Material High Strength, High Translucency, Dental Zirconia Blank

 

C-CERA HT high strength and high translucency, one of the best selling products series in the company, the material can be applied to coping , coping bridge, crown, all kinds of bridges. Suitable for restoration of both anterior and posterior for any kind of restoration cases.

 


High Strength Dental Zirconia Blank For Milling Implant Crowns 0

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Sintering


Every batch of zirconia block has gone though a completely sintering test. The sintering methods have a great impact on blocks’ properties, such as translucency, dyeing results, strength, hardness and ageing resistance, which will affect the blocks’ final stability. Therefore, please follow the sintering curve of it.
The translucency of restorations is closely related to sintering temperature and regular maintenance of sintering furnace. Please follow the below temperature chart.

 

High Strength Dental Zirconia Blank For Milling Implant Crowns 1

High Strength Dental Zirconia Blank For Milling Implant Crowns 2

 

High Strength Dental Zirconia Blank For Milling Implant Crowns 3

 

To achieve expected quality, the sintering curves must be followed.


Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.

 

 

1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.

3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.

 

 

 

 

 

 

 

 

 

 