| Place of Origin: | China Shenzhen |
|---|---|
| Brand Name: | XTCERA |
| Certification: | CE FDA |
| Model Number: | 3D White |
| Minimum Order Quantity: | 50 |
| Price: | Negotiable |
| Packaging Details: | Box |
| Delivery Time: | 5-8 working days |
| Payment Terms: | T/T |
| Supply Ability: | 3000pcs/week |
| Material: | Zirconia | Translucent: | 43%-55% |
|---|---|---|---|
| Flexural Strength: | 1100mpa-750mpa | Thickness: | 10-25mm |
| Color: | White | ||
| High Light: | 1250HV Zirconia Teeth Crowns Blank,1100mpa Zirconia Teeth Crowns Blank,55% Translucent Zirconia Blank Material |
||
Unique 3D White, which leaves you more space of dyeing and imagination!
| layer | Proportion |
Vickers Hardness(HV) |
Strength(MPa) | Translucency |
| layer 1 | 20% | ≥1250 | ≥750 |
55%
↑
43% |
| layer 2 | 20% | ≥1270 | ≥920 | |
| layer 3 | 20% | ≥1290 | ≥950 | |
| layer 4 | 20% | ≥1310 | ≥1000 | |
| layer 5 | 20% | ≥1350 | ≥1100 |
Features:
Unique Dyeing System
White but Translucent with Natural Gradient
Flexible Coloring to Make Teeth More Natural
Indications
XTCERA 3D White is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three uints, inlays, and onlays for anterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.
Chemical Composition
| Component | Content |
| ZrO2+HfO2 | ＞90.5wt% |
| Y2O3 | 9.28wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.5wt% |
Properties
| Projects | Detection result |
| Sintering Density | ≥6.0g/cm³ |
| Bending Strength | ≥750MPa |
| Vickers Hardness | 1250HV |
| Chemical Solubility | ＜100μg/m² |