3D Multilayer Dental Zirconia Block Natural Gradient High Transmittance

Basic Information
Place of Origin: China
Brand Name: XTCERA
Certification: CE, FDA, ISO
Model Number: TT
Minimum Order Quantity: 50
Price: Negotiable
Packaging Details: Box Package
Delivery Time: 10working days
Payment Terms: T/T, Western Union
Supply Ability: 1500pcs/day
Detail Information
Name: Zirconia Dental Material Type: Denture Material
Vickers Hardness: 1250HV Chemical Solubility: <100μg/m²
ZrO2+HfO2: >94wt% Y2O3: 5.3wt%
High Light:

dental zirconia blank

,

zirconia dental material


Product Description

3D Multilayer Zirconia Blanks

 

Our zirconia blocks are compatible with different kinds of CAD/CAM system and manual system, such as Cercon system, Sirona Inlab system, KaVo system, Wieland system and Amann Girrbach AG system.
We choose the best zirconia powder and utilize a cold isostatic pressing system to form shapes,the main advantage of isostatic pressing is the uniform application of pressure, which lead to a very homogeneous density and shrinkage,yielding a very reproducible process.The production cost by using isostatic pressing is much higher than uniaxel dry pressing, but quality is also much higher.We try to provide high quality ,low cost zirconia blocks for all dental CAD/CAM milling system, support open architecture CAD/CAM milling system. We will sell lowest price on zirconia blocks and highest quality to all labs worldwide.

 

 

Simply to be Natural

 

Layer Proportion

Vickers

Hardness(HV)

Strength(MPa) Color Translucency
Layer 1 30% ≥1250 ≥750 ,≤1250

Shallow

 

 

Deep

43%—55%
Layer 2 15%
Layer 3 15%
Layer 4 20%
Layer 5 20%

 

Characteristics:

Natural Color Transition, Pre-colored.

Top High Transmittance with Natural Gradient

Simple and Less Process of Production

 

Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA 3D multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three units, inlays, and onlays for anterior and posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.

 

 

Chemical Composition

 

ZrO2+HfO2 >94wt%
Y2O3 5.3wt%
AL2O3 <0.5wt%
Other Oxides <0.5wt%

 

Properties

Sintering Density :6.0g/cm³
Bending Strength:≥750MPa
Vickers Hardness:1250HV
Chemical Solubility:<100μg/m²

 

 

Sintering step Temperature range(℃) Time(h)
paragraph 1 20-900 1.5
paragraph 2 900-900 0.5
paragraph 3 900-1530 4.0
paragraph 4 1530-1530 2.0
paragraph 5 1530-800 2.0
paragraph 6 800-Natural cooling 100 Draw a charge