| Material: | Zirconia | Translucent: | 43% |
|---|---|---|---|
| Flexural Strength: | 1250mpa | Thickness: | 10-25mm |
| Color: | White | CTE: | Complied |
| Radioactivity: | Complied | Vickers Hardness: | 1298Hv |
| High Light: | High Strength Translucent Zirconia Blocks,1250mpa Translucent Zirconia Blocks,CTE Dental Cad Cam Blank |
||
X-CERA HT: High strength and translucency, apply to coping, coping bridge, all kinds of bridges!
XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over 30,000 square meters R&D and production base.
Our zirconia block is made of nanometer medical grade zirconia powder.
The powder is firstly compacted by cold isostatic pressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.
The zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.
System compatible
Chemical Composition
| Component | Content |
| ZrO2+HfO2 | ＞90.5wt% |
| Y2O3 | 9.28wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.5wt% |
Properties
| Projects | Detection result |
| Sintering Density | ≥6.0g/cm³ |
| Bending Strength | ≥750MPa |
| Vickers Hardness | 1250HV |
| Chemical Solubility | ＜100μg/m² |