| Sintering Density: | ≥6.0g/cm³ | Bending Strength: | ≥750MPa |
|---|---|---|---|
| Transmittance: | 55% | Vickers Hardness: | 1250HV |
| Size: | Customer Size | Usage: | PROFESSIONAL DENTAL |
| High Light: | ultra translucent zirconia,cerec zirconia blocks |
||
Multilayer TT Zirconia Blanks
Advantage of zirconia dental:
1. High aesthetic effect, good transparency, natural tooth color.
2. High strength, hardness and durable, do not need the support of metal.
3. Excellent biological compatibility, no metal odor, no black color and no corrosion, anti allergy, protect the gums and avoid bleeding.
The zirconia disk and blocks are the finest and most pure zirconia materials , most of zirconia powder are from Japan and well compatible with all open cad cam milling machine,like Origin milling machine,Shera Milling machine.VHF milling machine.
1.All of zirconia disks with super high translucence (light transmittance 40%) are for full contour.
2.All of zirconia block with High translucence (light translucence 30%) are for dental coping and bridge.
Perfect Your Smile!
| Layer | Proportion |
Vickers |
Strength(MPa) | Color | Translucency |
| Layer 1 | 30% | ≥1250 | ≥750 |
Shallow |
55% |
| Layer 2 | 15% | ||||
| Layer 3 | 15% | ||||
| Layer 4 | 20% | ||||
| Layer 5 | 20% |
Characteristics:
Top High Transmittance
Natural Color Transition, Pre-colored.
Simple and Less Process of Production
Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA TT Multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, inlays and onlays restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.
Chemical Composition
| Component | Content |
| ZrO2+HfO2 | ＞90.5wt% |
| Y2O3 | 9.28wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.5wt% |
Properties
| Projects | Detection result |
| Sintering Density | ≥6.0g/cm³ |
| Bending Strength | ≥750MPa |
| Transmittance | 55% |
| Vickers Hardness | 1250HV |
| Sintering step | Temperature range (℃) | Time(h) |
| paragraph 1 | 20-900 | 1.5 |
| paragraph 2 | 900-900 | 0.5 |
| paragraph 3 | 900-1450 | 3.0 |
| paragraph 4 | 1450-1450 | 2.0 |
| paragraph 5 | 1450-800 | 1.0 |
| paragraph 6 | 800-Natural cooling 100 | Finished |